Application of Friction Surfacing to the Production of Aluminum Coatings Reinforced with Al2O3 Particles
AUTOR(ES)
Oliveira, Pedro Henrique Fernandes, Galvis, Juan Carlos, Martins, Juliana de Paula, Carvalho, André Luis Moreira
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
13/11/2017
RESUMO
The aim of this work was to produce deposits of AA6351-T6, reinforced with alumina (Al2O3) particles, over a substrate of AA5052-H32 through friction surfacing. AA6351-T6 consumable rods were drilled with one and two holes, which were filled with Al2O3 particles posteriorly. To perform the deposition, a conventional KONE KFE-3/BR milling machine was used. The results showed that Al2O3 particles increase the hardness values of the produced deposits when compared to those without particle addition. The coatings presented a fine equiaxed grain size distribution, once the grain refinement was nearly 48% lower than the as-received material. Moreover, deposit regions that showed finer grain boundaries also showed a higher volume fraction, which can be related to the particle stimulated phenomenon. Electron backscatter diffraction results showed the occurrence of low angle grain boundary substructures and lattice rotation, indicating that the material undergoes dynamic recrystallization during friction surfacing.
Documentos Relacionados
- Using ZrO2 or Al2O3 particles to enhance the mechanical properties of a LZSA glass-ceramic matrix
- Properties of SiC Ceramics Sintered via Liquid Phase Using Al2O3 + Y2O3, Al2O3 + Yb2O3 and Al2O3 + Dy2O3 as Additives: a Comparative Study
- Síntese e caracterização do compósito Al2O3 -YAG e do Al2O3-YAG e Al2O3 aditivados com Nb2O5
- Heterojunction between Al2O3 and SnO2 thin films for application in transparent FET
- Fluência em filtros cerâmicos de Al2O3