Application of ftir in the determination of acrylate content in poly(sodium acrylate-co-acrylamide) superabsorbent hydrogels
AUTOR(ES)
Magalhães, Antônio Sávio G., Almeida Neto, Manuel P., Bezerra, Maslândia N., Ricardo, Nágila M. P. S., Feitosa, Judith P. A.
FONTE
Química Nova
DATA DE PUBLICAÇÃO
2012
RESUMO
Hydrogels have been prepared by free-radical solution copolymerization of acrylamide and sodium acrylate (NaAc), with molar ratio ranging from 25/75 to 80/20, respectively, using methylene bisacrylamide as the crosslinking agent. A FTIR spectroscopy procedure to determine the acrylate/acrylamide ratio in these hydrogels was proposed based on absorbance at 1410 cm-1 (nCOO-) and 2940 cm-1 (nCH and nCH2). A straight line with a good linear correlation coefficient (0.998) was obtained by plotting the acrylate content (Ac%) versus relative absorbance (Arel = A1410/A2940). Results were confirmed by the amount of sodium cation released in acid medium determined by atomic absorption spectrometry.
Documentos Relacionados
- Synthesis and properties of collagen-g-poly(sodium acrylate-co-2-hydroxyethylacrylate) superabsorbent hydrogels
- NOVEL SUPERABSORBENT HYDROGEL COMPOSITE BASED ON POLY(ACRYLAMIDE-CO-ACRYLATE)/NONTRONITE: CHARACTERIZATION AND SWELLING PERFORMANCE
- Synthesis and characterization of pH and temperature responsive poly(2-hydroxyethyl methacrylate-co-acrylamide) hydrogels
- Determination of polymer content in energetic materials by FT-IR
- Factorial design to obtain magnetized poly(ethyl acrylate-co-divinylbenzene)