Avaliação in vitro da Microinfiltração na Interface da Parede Gengival das Caixas Proximais em Cavidades Classe II de Molares Decíduos, Restaurados com Resina Composta Auto e Fotopolimerizável / ANALYSIS IN VITRO OF MICROLEAKINGS ON GUMS EDGES OF THE APPROXIMAL BOXES IN CLASS II CAVITIES OF DECIDUOUS MOLARS, RESTORED WITH AUTO AND LIGHT-CURED COMPOSITE RESIN
AUTOR(ES)
Alessandro Leite Cavalcanti
DATA DE PUBLICAÇÃO
1997
RESUMO
The purpose of this study was evaluation in vitro of marginal microleakings, present on gums edges of class II cavities of deciduous molars, restored with composite resin (auto and light-cured), with the use of a staining solution to verify the leaking. Cavities prepared presented enamel on gums edges and were restored according to four different techniques: lightcured composite resin; auto-cured composite resin; mixed technique (auto and light-cured composite resin) and glass-ionomer/composite resin. Next, we proceeded to thermo-cycling (5°C and 55°C, 700 cycles), turning impermeable, immersion in staining solution and slicing. The microleaking evaluation was done according to a pre-established scale (from 0 a 4 degrees). After the statical analysis of the results, it was concluded that all the groups presented microleaking, in varying degrees. However, the groups which used the mixed technique and light-cured resin presented the smallest levels of leaking, and microleaking was not observed on the auto-cured composite resin/light-cured composite resin edge.
ASSUNTO(S)
deciduous tooth composite resin dente decíduo microleakage microinfiltração resina composta
Documentos Relacionados
- Avaliação da microinfiltração marginal em cavidades classe II de molares decíduos restauradas com diferentes cimentos de ionômero de vidro
- Clinical wear of approximal glass ionomer restorations protected with a nanofilled self-adhesive light-cured protective coating
- Avaliação in vitro da resistência à fratura de cavidades classe II restauradas pela técnica do tratamento restaurador atraumático (ART)
- Avaliação in-vitro da microinfiltração em cavidades classe II restauradas com composito de alta viscosidade submetidas a carregamento oclusal ciclico
- Avaliação biomecânica de pré-molares superiores restaurados com diferentes monômeros resinosos