Characterization of the structural and magnetic properties of Nd16Co76-xRu xC7B alloys
AUTOR(ES)
Paduani, C., Valcanover, J. A., Ardisson, J. D., Samudio Pérez, C. A., Yoshida, M. I.
FONTE
Brazilian Journal of Physics
DATA DE PUBLICAÇÃO
2007-09
RESUMO
The Nd16Co76-xRu xC7B system has been investigated to assess the effect of boron-carbon combined addition on the ferromagnetic behavior of these intermetallic compounds. The results indicate that the addition of 1 at.% B favors the formation of the tetragonal magnetic phase 2:14:1 in these alloys. With the increase of the Ru concentration is observed an expansion of the lattice in the basal plane as well as a contraction along the c direction of the tetragonal unit cell. The Curie temperature decreases from 432 K at x = 6 to 421 K for x = 27, whereas the saturation magnetization has a steep decrease. The highest T C value has been verified for the alloy with the largest c parameter, despite its a parameter is the smallest one. In comparison to isotypic borides and pure carbides, a loss of coercivity and remanence is observed.
Documentos Relacionados
- An investigation of structural and magnetic properties of the Nd16Co72-xRu xC11B coro-carbides
- Structural and magnetic properties of the half-ferromagnetic Co2+x+yMn1-xAl1-y alloys
- Magnetic, structural and superconducting properties of MgC(Ni1 - xFe x)3
- Magnetic properties of electrodeposited Fe-poor Fe-Cu alloys
- Gate-controlled magnetic properties of the magnetic semiconductor (Zn,Co)O