Dependence of crystalline, ferroelectric and fracture toughness on annealing in Pb(Zr0.52Ti0.48)O3 thin films deposited by metal organic decomposition
AUTOR(ES)
Zheng, Xuejun, Zhou, Yichun, Yan, Zhi
FONTE
Materials Research
DATA DE PUBLICAÇÃO
2003-12
RESUMO
Crystalline, electric and fracture properties of Pb(Zr0.52Ti0.48)O3 (PZT) thin films are strongly affected by annealing temperatures in rapid treatment annealing (RTA) of metal organic decomposition (MOD). X-ray diffraction (XRD), RT66A standard ferroelectric analyzer and Vickers indentation method were used to investigate the crystalline, ferroelectric and mechanical properties, respectively. PZT thin film with complete perovskite structure and best ferroelectric property can be obtained at 750 °C, however the fracture toughness was weaker than the thin films annealed at 600 °C and 650 °C. With the increase of annealing temperature from 600 °C to 750 °C, the remanent polarization and coercive field increased in the ranges 13.8~25.2 (µC/cm²) and 7.2~8.3 (kV/cm) respectively, while the fracture toughness of PZT thin films decreased from 0.49 MPam½ to 0.47 MPam½.
Documentos Relacionados
- Espalhamento intervales na liga Al0.48Ga0.52As
- Growth of the In0.53Ga0.47As/ In0.52Al0.48As on InP by MBE
- Spray Deposited Nanostructured CuO Thin Films: Influence of Substrate Temperature and Annealing Process
- Characterization of TiCN thin films deposited by Dc-Pulsed PACVD using methane precursor
- Fracture toughness in metal matrix composites