Efecto del tiempo de superpulso de soldadura sobre la evolución microestructural de un acero de bajo carbono
AUTOR(ES)
Gualco, Agustín, Raad, Franco, Zappa, Sebastián
FONTE
Matéria (Rio J.)
DATA DE PUBLICAÇÃO
19/07/2018
RESUMO
ABSTRACT The Super Pulse arc type was developed to provide a solution to butt root pass beads in the semi-automatic welding process with gas protection (GMAW). Unlike standard pulse welding, the Super Pulse uses a sequence of different pulse waveforms to create a cord shape and appearance similar to the GTAW process. It uses higher amperage in the primary phase to improve penetration and low amperage in the second phase to reduce the heat input. Spray transfer is used in the primary phase to improve penetration and short arc in the secondary phase to cool the solder bath giving less heat transfer and less distortion to the base material. In the literature there is little information regarding the relationship between the Super Pulse variables and the microstructural characteristics of the deposited metal. The objective of this work was to evaluate the influence of the times of each phase in Super Pulse mode, on the geometric characteristics of the cord and the solidification in weld deposits of low carbon steels. For this purpose, strands should be welded on an IRAM - IAS U500 42 - F24 plate by varying the phase time of the Super Pulse. In cross sections, the geometry of the bead was determined and in longitudinal sections, the microstructure and the characteristics of the molten and affected areas were determined. Preliminary results showed that bead geometry and solidification were strongly influenced by pulse parameters.
Documentos Relacionados
- Evolución microestructural de un acero inoxidable superdúplex bajo ciclos térmicos de corta duración
- Estudio de la evolución microestructural durante el austenizado de un acero ASTMA335 P91
- Efecto de los ciclos térmicos sobre la ZAT de una soldadura multipasos de un acero inoxidable superdúplex SAF 2507
- Efecto de la concentración del silano MTMO sobre la protección contra la corrosión de acero electrocincado
- Efecto del procedimiento de soldadura por FSW en la evolución temporal de las propiedades en uniones de AA 7075-T651