Efeito do tratamento térmico na microestrutura, turbostraticidade e superfície de carbono vítreo reticulado analisado por XPS, espalhamento Raman e voltametria cíclica

AUTOR(ES)

Gonçalves, Emerson Sarmento, Rezende, Mirabel Cerqueira, Baldan, Maurício Ribeiro, Ferreira, Neidenêi Gomes

FONTE

Química Nova

DATA DE PUBLICAÇÃO

2009

RESUMO

The structural and surface properties of reticulated vitreous carbon (RVC) were discussed as a function of its heat treatment temperature (HTT), for samples produced in the range from 700 to 2000 ºC, using the furfuryl precursor resin. The samples were analyzed by x-ray photoelectron spectroscopy, first and second order Raman scattering as well as electrochemical response. Exploring the material turbostraticity concept, the interdependence between the RVC chemical surface variation and its defects were demonstrated. The influence of heteroatom presence was discussed in the material ordering for HTT lower than 1300 ºC while the graphitization process evolution was also pointed out for HTT higher than 1500 ºC.

Documentos Relacionados

• Obtenção e caracterização de carbono vítreo reticulado
• Remocao de cobre (II) em eletrodos de platina-polipirrol e carbono vitreo reticulado
• Remoção de íons Cd2+ de soluções aquosas por eletrodeposição em eletrodos de carbono vítreo reticulado
• Obtenção de um material adsorvente para íons de metais pesados, através da eletropolimerização de 2-mercaptobenzimidazol à superfície de carbono vítreo reticulado
• Efeitos dos laminados a quente e a morno na microestrutura, textura e propriedades de aços baixo carbono