Evaluation of the Influence of MgO and La2O3 on the Fast Sintering of Mullite
AUTOR(ES)
Souto, Pollyane Márcia de, Menezes, Romualdo Rodrigues, Kiminami, Ruth Herta Goldschmidt Aliaga
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
2015-02
RESUMO
The influence of MgO and La2O3 on the fast sintering of mullite was evaluated in this work. High-purity mullite was doped with MgO and La2O3, conventionally sintered, fast sintered, and microwave-sintered in rapid sintering cycles. The results showed that MgO and La2O3 strongly affected the densification of fast sintered samples; and only doped bodies reached high densities when fast sintered. However, the densification behavior of doped samples was dependent on the amount of sintering aids. MgO doped samples presented better densification behavior than La2O3 doped samples. Microwave-processed samples required a balance between power, time and amount of additives to obtain highly dense and homogenous microstructures.
Documentos Relacionados
- Microwave sintering of mullite-Al2O3 from kaolin precursor
- MgO Saturation Analisys of CaO-SiO2-FeO-MgO-Al2O3 Slag System
- Compósitos à base de Al2O3, com adições de NbC e de MgO
- Theoretical studies of the EPR parameters for Ni2+ and Co+ in MgO
- Identificação e avaliação dos mecanismos de ataque da escória SiO2-CaO-Al2O3-MgO em tijolos refratários de MgO-C