Evaluation through the mgnetic inspection of the superficial condition of steel bearing rings DIN 100Cr6 after hard and dry turning. / Avaliação através da inspeção magnética da condição superficial de anéis de rolamento de aço DIN 100Cr6 após torneamento duro a seco.

AUTOR(ES)
DATA DE PUBLICAÇÃO

2008

RESUMO

The present work presents information for the manufacturing of ball bearings components with higher limits of resistance to fatigue, enabling a longer useful life and also the optimization of the production of the pieces, making the usual and final process of grinding unnecessary, which would result in a costs reduction. The motivations of this study are the generation of compressive high residual stress in the hard-dry turning at high speeds, the application of the MBN as technique of measurement of the residual stress in steel 100CrMn6, and the optimization of the quality/costs in the manufacturing of ball bearings. In order to achieve these purpose, the work will study the influence of the machining parameters (cutting speed (Vc), feed rate (a), depth of cut (p), and wear of tool (VB)) in the generation of the superficial residual tensions and also the turning forces (Fc, Fa, Fp), in internal conical rings of ball bearings of steel 100CrMn6 thermally hardened, seeking to find a correlation between the stress of the tool and the referred efforts. In the experimental phase, a complete factorial planning will be used to perform the tests and measurements projected. In the turning tests, the cutting forces will be measured using a piezoelectric dynamometer. After that, measurements of superficial roughness will be performed. Also, the study of the microstructure will be made through the metallographic analysis. The residual tensions will be measured using the strain gage hole-drilling method and the measurement of the superficial microestrutural alterations will be carried out using the technical of the magnetic Barkhausen noise (MBN). The values of residual tension obtained by the hole-drilling will be correlated with the RMB.

ASSUNTO(S)

magnetic barkhausen noise hard turning ruído magnético de barkhausen high speed turning ensaios magnéticos não destrutivos tensão residual tool wear residual stress processos de fabricação machining forces

ACESSO AO ARTIGO

Documentos Relacionados