Hydrogen gas permeation through amorphous and partially crystallized Fe40Ni38Mo4B18
AUTOR(ES)
Ribeiro, Rafaella Martins, Lemus, Luis Fernando, Santos, Dilson Silva dos
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
30/08/2012
RESUMO
Samples of amorphous and partially crystallized Fe40Ni38Mo4B18 alloy were submitted to hydrogen gas permeation from 523 to 643 K. The hydrogen permeation curves exhibited a single sigmoidal shape, typical of tests where no hydride formation occurs. It was observed that the hydrogen diffusivity increases for the amorphous samples and partially crystallized alloy with the temperature increase. The hydrogen diffusion coefficient as a function of temperature was found to be D = 5.1 ± 0.5 × 10-12 exp (-11.0 ± 3.5/RT) (m².s-1) for amorphous condition and D = 3.6 ± 0.5 × 10-11 exp (-19.8 ± 3.3/RT) (m².s-1) for the partially crystallized condition. This suggests that the annihilation of defects in the amorphous structure and the crystalline phase precipitate contributes to the increase of the hydrogen diffusion.
Documentos Relacionados
- Optimization of operational parameters and bath control for electrodeposion of Ni-Mo-B amorphous alloys
- Electrodeposition of Ni-Mo and Fe-Mo alloys from sulfate-citrate acid solutions
- Estudo da eletrodeposição de ligas Fe-Ni-Mo e Fe-Ni-W com aplicações tecnológicas
- Crystallization Behavior of Amorphous Ti51.1Cu38.9Ni10.0 Alloy
- RECIPITATION PROCESSES CONTROLLED BY LATTICE AND GRAIN BOUNDARY DIFFUSION IN ALLOY 33 (FE-NI-CR-MO-N)