Influence of deformation on the kinetics of phase transformation in a forging steel during warm working
AUTOR(ES)
Oliveira, Mauro Aparecido Ferreira de, Jorge Jr, Alberto Moreira, Balancin, Oscar
FONTE
Materials Research
DATA DE PUBLICAÇÃO
2004-06
RESUMO
Dilatometric techniques were used to determine the start and finish transformation heating temperatures for a carbon steel (0.30% C - 1.5% Mn). The mechanical behavior of the steel was measured by torsion testing in the temperature range of 700 to 820 °C with holding times ranging from 1 to 30 min. The flow stress curves presented different shapes and stress levels. These differences were attributed to the ferrite and pearlite, ferrite and austenite, and austenite strained structures. When ferrite and pearlite were deformed together, the flow stress presented a hump with little straining; when the austenitic structure was deformed the shape of the flow stress curve was typical of materials having low stacking fault energy. The microstructural evolution observed by optical and scanning electron microscopy revealed that the evolution of the phase transformation was dependent on the testing temperatures, holding times and amount of straining. Comparisons were made on the kinetics of phase transformation with and without the application of plastic deformation, and evidence of strain-induced dynamic transformation was investigated.
Documentos Relacionados
- Effects of deformation on the microstructure of a Ti-V microalloyed steel in the phase transition region
- The influence of plastic deformation on the structure of passive films on carbon steel in simulated pore solution
- Kinetics of sigma phase formation in a Duplex Stainless Steel
- Deformation induced precipitation in an industrial Ti microalloyed dual phase steel
- Effect of Hot Deformation on Microstructure, Hardness and Precipitation Kinetics in a C350 Maraging Steel Modified by Titanium Addition