Influence of the final temperature of investment healting on the tensile strength and Vickers hardness of CP Ti and Ti-6Al-4V alloy
AUTOR(ES)
Oliveira, Pedro César Garcia, Adabo, Gelson Luis, Ribeiro, Ricardo Faria, Rocha, Sicknan Soares da, Ávila, Fabiano Araújo, Valle, Accácio Lins do
FONTE
Journal of Applied Oral Science
DATA DE PUBLICAÇÃO
2007-02
RESUMO
The aim of the work was to evaluate the influence of the temperature of investment healting on the tensile strength and Vickers hardness of CP Ti and Ti-6Al-4V alloy casting. Were obtained for the tensile strength test dumbbell rods that were invested in the Rematitan Plus investment and casting in the Discovery machine cast. Thirty specimens were obtained, fiftten to the CP Titanium and fifteen to the Ti-6Al-4V alloy, five samples to each an of the three temperatures of investment: 430ºC (control group), 480ºC and 530ºC. The tensile test was measured by means of a universal testing machine, MTS model 810, at a strain of 1.0 mm/min. After the tensile strenght test the specimens were secctioned, embedded and polished to hardness measurements, using a Vickers tester, Micromet 2100. The means values to tensile tests to the temperatures 430ºC, 480 and 530: CP Ti (486.1 - 501.16 - 498.14 -mean 495.30 MPa) and Ti-6Al-4V alloy (961.33 - 958.26 - 1005.80 - mean 975.13 MPa) while for the Vickers hardness the values were (198.06, 197.85, 202.58 - mean 199.50) and (352.95, 339.36, 344.76 - mean 345.69), respectively. The values were submitted to Analysis of Variance (ANOVA) and Tukey,s Test that indicate differences significant only between the materials, but not between the temperature, for both the materias. It was conclued that increase of the temperature of investment its not chance the tensile strength and the Vickers hardness of the CP Titanium and Ti-6Al-4V alloy.
Documentos Relacionados
- Vickers hardness of cast commercially pure titanium and Ti-6Al-4V alloy submitted to heat treatments
- Effect of plasma welding parameters on the flexural strength of ti-6al-4v alloy
- Evaluation of shot peening on the fatigue strength of anodized Ti-6Al-4V alloy
- Micromachinability study of Ti (CP) and Ti-6Al-4V alloy by means of single point diamond turning
- Effects of plasma immersion ion implantation (PIII) of nitrogen on hardness, composition and corrosion resistance of Ti-6Al-4V alloy