Influência de filmes de INCONEL 600, depositados por triodo-magnetron-sputtering, na resistência à corrosão de substratos de latão C360
AUTOR(ES)
Alexandre Werner Arins
DATA DE PUBLICAÇÃO
2006
RESUMO
The objective of this work is to evaluate the corrosion resistance of Brass C360 samples coated with INCONEL 600 films, obtained by the plasma at configuration Triodo agnetron Sputtering (TMS) technique. In order to compare had been deposited films with different parameters (time of deposition and potential to the substrate) obtaining coatings with different characteristics (thicknesses, density, porosity and stress in film). Brass samples electrochemical behavior was investigated by the consist of polarize the samples of immersed test in a solution of NaCl 3.5%, to evaluate the corrosion resistance of the samples. The results show that all INCONEL 600 the films improved its corrosion resistance to the Brass substrate being more efficient the films with more time of deposition and more potential applied in the substrate.
ASSUNTO(S)
metais sputtering brass engenharia de materiais e metalurgica corrosion inconel metals sputtering latão inconel corrosão
ACESSO AO ARTIGO
Documentos Relacionados
- Avaliação eletroquímica da resistência à corrosão de amostra de latão C360 recoberta com filmes de inconel 600, CR/NI E TINX via triodo-magnetrom- sputtering
- Propriedades supercondutoras de filmes finos de Nb depositados por magnetron sputtering
- Deposições reativas por Triodo-Magnetron-Sputtering: efeitos da malha da tela no processo de envenenamento do alvo e nas propriedades de filmes de TiN.
- Filmes de óxido de índio dopado com estanho depositados por magnetron sputtering.
- Desposição de filmes metálicos sobre a poli(Tereflalato de etileno) via Triodo-Magnetron- Sputtering: influência da corrente e das voltagem nas propriedades do filmes