Kinetic Analysis of the Decomposition of the KFe3(SO4)2-x(CrO4)x(OH)6 Jarosite Solid Solution in Ca(OH)2 Medium
AUTOR(ES)
Mireles, Ister, Reyes, Iván A., Flores, Víctor H., Patiño, Francisco, Flores, Mizraim U., Reyes, Martín, Acosta, Manuel, Cruz, Roel, Gutiérrez, Emmanuel J.
FONTE
J. Braz. Chem. Soc.
DATA DE PUBLICAÇÃO
2016-06
RESUMO
The decomposition of the solid solution of potassium jarosite with chromium(VI) in Ca(OH)2 media was studied in the present work. According to experimental results, the incorporation of CrO42- into the crystal structure of jarosite resulted in a solid solution with the following approximate formula: [K0.86(H3O)0.14]Fe2.67[(SO4)1.23(CrO4)0.77][(OH)5.01(H2O)0.99]. The experimental data describe a reaction based on the shrinking core model with chemical control for spherical particles. A reaction order of n = 0.67 and an activation energy (Ea) of 63.75 kJ mol-1 were obtained in the induction period (tind). The progressive conversion period is characterized by the diffusion of K+, SO42- and CrO42- ions into the solution. In this stage, n = 1.99 with respect to OH-, and Ea = 51.56 kJ mol-1. The CrO42- diffusion is slower compared to that of sulfate, a slight amount of chromate is adsorbed in the layer of the solid residue consisting on Fe(OH)3. Finally, the equations that satisfactorily describe the reaction process were established from the data obtained.
Documentos Relacionados
- Cinzas volantes álcali-ativadas com solução combinada de NaOH e Ca(OH)2
- Cinzas volantes álcali-ativadas com solução combinada de NaOH e Ca(OH)2
- Disinfection and outcome of root canal treatment using single-file or multifile systems and Ca(OH)2 medication
- Compound Effect of CaCO3 and CaSO4·2H2O on the Strength of Steel Slag - Cement Binding Materials
- Aspectos histomicrobiológicos do sistema de canais radiculares e das lesões periapicais em dentes de cães após instrumentação automatizada e medicação intracanal com pastas de Ca(OH)2