Microstructural path of recrystallization in a commercial Al-Mn-Fe-Si (AA3003) alloy
AUTOR(ES)
Rios, Paulo Rangel, Padilha, Angelo Fernando
FONTE
Materials Research
DATA DE PUBLICAÇÃO
2003-12
RESUMO
The phenomenological analysis of recrystallization data is described. The concept of microstructural path is briefly introduced as well as some of its relevant equations. The correct equation for the impingement compensated chord length is introduced and used here for the first time. The theory is then applied to data from the recrystallization of a commercial Al-Mn-Fe-Si (AA3003) alloy. It is concluded that nucleation is site saturated and that the grain boundary velocity decreases with time. The analysis also shows that the shape of the recrystallized regions significantly deviates from spherical as the reaction progresses, probably because of the boundary/precipitates interaction.
Documentos Relacionados
- Evolução da microestrutura e da textura durante o processamento de chapas da liga Al-Mn-Fe-Si (3003) produzidas por lingotamento contínuo: um estudo comparativo com o processo semi-contínuo.
- Microstructural evolution of AA7050 al alloy processed by ECAP
- Characterization of manganese alloy residues for the recycling of FeSiMn and high-carbon FeMn fines
- Processing, microstructural characterization and mechanical properties evaluation of the Al92Fe3Cr2Mn3 alloy
- Microstructural analysis in the Fe-30.5Mn-8.0Al-1.2C and Fe-30.5Mn-2.1Al-1.2C steels upon cold rolling