Precipitation reaction in alpha-Cu-Al-Ag alloys
AUTOR(ES)
Silva, R.A.G., Adorno, A.T., Carvalho, T.M., Magdalena, A.G., Santos, C.M.A.
FONTE
Matéria (Rio de Janeiro)
DATA DE PUBLICAÇÃO
2011
RESUMO
The Ag-rich precipitates formation reaction in the Cu-9.22%at. Al-4.66%at. Ag, Cu-9.31%at. Al-5.83%at. Ag and Cu-9.37%at. Al-7.08%at. Ag alloys was studied using microhardness change measurements with temperature and time, differential scanning calorimetry (DSC), scanning electron microscopy (SEM) and X-ray diffractometry (XRD). The results indicated that the Ag-rich phase formation is an interface controlled process with a zero-order mechanism, due to the amount of unsolved Ag that makes the precipitation reaction rate independent of Ag concentration.
Documentos Relacionados
- Phase Separation in Rapid Solidified Ag-rich Ag-Cu-Zr Alloys
- Reação de precipitação de Ag na liga Cu-8%Al-6%Ag
- Effect of phase transformations on hardness in Zn-Al-Cu Alloys
- Morphology and Phase Formation During the Solidification of Al-Cu-Si and Al-Ag-Cu Ternary Eutectic Systems
- Mechanical spectroscopy study of the Cu36Zr59Al5 and Cu54Zr40Al6 amorphous alloys