Production of selective membranes using plasma deposited nanochanneled thin films
AUTOR(ES)
Carvalho, Rodrigo Amorim Motta, Carvalho, Alexsander Tressino de, Silva, Maria Lúcia Pereira da, Demarquette, Nicole Raymond
FONTE
Materials Research
DATA DE PUBLICAÇÃO
2006-12
RESUMO
The hydrolization of thin films obtained by tetraethoxysilane plasma polymerization results in the formation of a nanochanneled silicone like structure that could be useful for the production of selective membranes. Therefore, the aim of this work is to test the permeation properties of hydrolyzed thin films. The films were tested for: 1) permeation of polar organic compounds and/or water in gaseous phase and 2) permeation of salt in liquid phase. The efficiency of permeation was tested using a quartz crystal microbalance (QCM) technique in gas phase and conductimetric analysis (CA) in liquid phase. The substrates used were: silicon for characterization of the deposited films, piezoelectric quartz crystals for tests of selective membranes and cellophane paper for tests of permeation. QCM analysis showed that the nanochannels allow the adsorption and/or permeation of polar organic compounds, such as acetone and 2-propanol, and water. CA showed that the films allow salt permeation after an inhibition time needed for hydrolysis of the organic radicals within the film. Due to their characteristics, the films can be used for grains protection against microorganism proliferation during storage without preventing germination.
Documentos Relacionados
- Characterization of TiCN thin films deposited by Dc-Pulsed PACVD using methane precursor
- Electrochemical Behavior of Titanium Nitride Thin Films Deposited on Silicon by Plasma Discharge Technique in Cathodic Cage
- Analysis of SiO2 Thin Films Deposited by PECVD Using an Oxygen-TEOS-Argon Mixture
- Characterization of SiC thin films deposited by HiPIMS
- Plasma-deposited a-C(N): H films