Propriedades fisicas do monocristal fe/mgo(100) e estudo da expansao termica da superficie da ag(100)
AUTOR(ES)
Charlie Salvador Gonçalves
DATA DE PUBLICAÇÃO
2010
RESUMO
In this work we have developed a way to grow Fe/MgO(100) monocrystals by magnetron sputtering DC. We investigated the growing in a temperature range among 100 oC and 300 oC. Structural and magneto-crystalline properties were studied by dierent experimental techniques. Thickness and surface roughness of the lms were investigated by atomic force microscopy, while magneto-crystalline properties were investigated by magneto-optical Kerr eect and ferromagnetic resonance. Our results show that as we increase the deposition temperature, the magneto-crystalline anisotropy of the lms also increases, following the equation of Avrami. The best temperature value to make a lm is 300 oC. As the main result, we built a base of magnetoresistence devices and as an aplication, we present measurements of Fe/Cr/Fe trilayer coupling. In a second work we investigated the temperature dependence of the rst three interlayer spacings of Ag(100) surface using low energy electron diraction. A linear expansion model of crystal surface was used and the values of Debye temperatures of the rst two layers and thermal expansion coecient were determinated. A relaxation of 1% was found for Ag(100) surface and these results are matched with faces (110) and (111) of the silver. iv
ASSUNTO(S)
filmes monocristalinos propriedades estruturais ectroscopia propriedades magnéticas ressonância ferromagnética fisica thin films monocrystalline films spectroscopy magnetic properties ferromagnetic resonance
Documentos Relacionados
- Crescimento de filmes nanométricos monocristalinos de Fe/MgO(100) por "SPUTTERING" DC
- Estudo in-situ de filmes ultrafinos de óxidos de ferro sobre Ag(100) por técnicas de superfície
- Modificação térmica nas propriedades físicas da madeira
- Estudo da qualidade da carne ovina do nordeste brasileiro: propriedades físicas e sensoriais
- Estudo da desativação do agente VX usando o MgO por cálculos ab initio