Structural characterization and ferroelectric properties of strontium barium niobate (Sr xBa1-xNb2O6) thin films

AUTOR(ES)

Mendes, R.G., Araújo, E.B., Eiras, J.A.

FONTE

Materials Research

DATA DE PUBLICAÇÃO

2001

RESUMO

Strontium barium niobate (SBN) thin films of good quality were deposited on Pt/Ti/SiO2/Si substrate using a polymeric resin containing metallic ions. Films were crystallized at different temperatures and for different duration of time. The structure of these films was studied using X-ray diffraction. The coexistence of SrNb2O6 (SN) and SBN was observed in films crystallized at 700 °C. The amount of SN decreases when the crystallization time increases. Ferroelectric properties were determined for films crystallized at 700 °C for 1 and 5 h. For SBN film crystallized at 700 °C for 1 h, the remanent polarization (Pr) and the coercive field (Ec) were 2.6 muC/cm² and 71.9 kV/cm, respectively. For the film crystallized at 700 °C for 5 h these parameters were Pr = 1.1 muC/cm² and Ec = 50.5 kV/cm.

Documentos Relacionados

• Características estruturais, microestruturais, dielétricas e piroelétricas de cerâmicas de Sr xBa1-X Nb2O6 forjadas a quente
• Structure Refinement of (Sr,Ba)Nb2O6 Ceramic Powder from Neutron and X-Rays Diffraction Data
• Estudo das propriedades dielÃtricas e magnÃticas da matriz compÃsita: SrBi2Nb2O9(SBN)X-BaFe12O9(BFO)1-X.
• Conductivity fluctuation of YBa2Cu3O7 - delta/Sr2YSbO6/SrTiO3 thin films
• Síntese, caracterização elétrica e estrutural de cerâmicas ferroelétricas de composição Ba0,90R0,10Ti1-xZrxO3 (R=Ca, Sr)