The effect of aggregate aspect ratio and temperature on the fracture toughness of a low cement refractory concrete
AUTOR(ES)
Prata, Laura Brum, Libardi, Walter, Baldo, João Baptista
FONTE
Materials Research
DATA DE PUBLICAÇÃO
2003-12
RESUMO
This work investigated the influence of the aggregate's aspect ratio on the fracture behavior of a low cement aluminum silicate refractory castable treated at two different temperatures (110 °C and 1000 °C). The aggregates were cylindrical pellets with an aspect ratio of 1, 2, 3 and 4, produced by extruding a mixture of clay and calcined alumina fired at 1600 °C for 4 h to yield mullite (3Al2O3.2SiO2). The behavior of the R-Curve and other relevant fracture parameters were evaluated based on the "Two Parameter Fracture Model" in a three-point flexure test of single-edge straight through notched specimens. The two temperature treatments produced different degrees of matrix-aggregate adhesion. The larger aspect ratio aggregates were found to promote toughening only in the dried condition, at 110 °C, while the specimens fired at 1000 °C for 4 h, regardless of their aggregate aspect ratio, displayed no significant toughening. The best results for fired samples, however, were obtained from specimens containing conventional angular aggregates.
Documentos Relacionados
- Experimental investigation on the effects of recycled aggregate on fracture behavior of polymer concrete
- THE DYNAMIC ANALYSIS OF LOW-ASPECT-RATIO AIRPLANE WINGS
- Effect of RAP content on flexural behavior and fracture toughness of flexible pavement
- Investigation on the Effect of Different Pre-Cracking Methods on Fracture Toughness of RT-PMMA
- Experimental investigations on mode II fracture of concrete with crushed granite stone fine aggregate replacing sand