The Structural and the Magnetic Properties of Aluminum Substituted Yttrium Iron Garnet
AUTOR(ES)
Mohaidat, Qassem I., Lataifeh, Mahdi, Hamasha, Khozima, Mahmood, Sami H., Bsoul, Ibrahim, Awawdeh, Mufeed
FONTE
Mat. Res.
DATA DE PUBLICAÇÃO
15/03/2018
RESUMO
In this paper, Y3AlxFe5-xO12 powders with x = 0.0, 0.2, 0.4, 0.6, 0.8, and 1.0 were prepared via solid state reaction method. X-ray diffraction, Vibrating Sample Magnetometry, and Mössbauer Spectroscopy were used to study their structural and magnetic properties. The XRD patterns of the samples show single phase structure with decreasing lattice constant when increasing Al concentration. The saturation magnetization decreases from 28.0 to 10.1 emu/g with increasing Al3+ from 0.0 to 1.0 due to the reduction of the superexchange interactions between iron ions in the a and d sublattices. Room temperature Mössbauer spectra for the samples were collected and analyzed. The hyperfine field values for octahedral and tetrahedral sites of the samples decreased with increasing Al concentration. Moreover, Mössbauer results have shown that Al3+ ions prefer to replace Fe+3 at the octahedral sites.
Documentos Relacionados
- Bronchoscopic management of tracheal lesions using the neodynium yttrium aluminium garnet laser.
- Investigation of Structural, Morphological, Magnetic Properties and Biomedical applications of Cu2+ Substituted Uncoated Cobalt Ferrite Nanoparticles
- Surface, catalytic, and magnetic properties of small iron particles: The effect of chemisorption of hydrogen on magnetic anisotropy*
- Y3+ substituted Sr-hexaferrites: sol-gel synthesis, structural, magnetic and electrical characterization
- Properties and structural features of iron doped BABAL glasses