Xylobolus frustulatus Decay of Oak: Patterns of Selective Delignification and Subsequent Cellulose Removal †
AUTOR(ES)
Otjen, Lewis
RESUMO
Xylobolus frustulatus caused a distinct pocket rot in decorticated oak. Polymerization products appeared to accumulate in advance of delignified wood to form barriers to decay. Medullary ray parenchyma and earlywood vessels were not readily degraded and remained between pockets of decay. Chemical analyses indicated that 97% lignin, 96% xylose, and 69% mannose were removed from pockets of wood during incipient decay. Although 53% of the cellulose was removed from these areas, the remaining white tissues were composed of relatively pure cellulose. Hyphae became abundant as the released cellulose was subsequently removed. In the most advanced stages of decay, hyphae were absent from pockets, and only a sparse lining of crystals, found to contain a high concentration of calcium, remained.
ACESSO AO ARTIGO
http://www.pubmedcentral.nih.gov/articlerender.fcgi?artid=239746Documentos Relacionados
- Delignification of Wood Chips and Pulps by Using Natural and Synthetic Porphyrins: Models of Fungal Decay †
- Selective Delignification of Aspen Wood Blocks In Vitro by Three White Rot Basidiomycetes †
- Removal of porphyrins from diphtheria toxoid by selective adsorption on Ecteola-cellulose.
- Comparative Studies of Delignification Caused by Ganoderma Species †
- Tyrosinase Reaction and Subsequent Chitosan Adsorption for Selective Removal of a Contaminant from a Fermentation Recycle Stream