Ceramic Matrix Composites
Mostrando 1-12 de 31 artigos, teses e dissertações.
-
1. Microstructure and diametral fracture strength of spark plasma sintered WC-6Co-0.2B and WC-6Co-0.5B ceramic composites from nanosized and metastable WC powders
Abstract The present work aimed at evaluating the microstructures and mechanical properties of spark plasma sintered WC-6 wt% Co ceramic composites doped with boron (0.2 and 0.5 wt%). W-50 at% C (W-6.13 wt% C) powders produced under different milling times (20, 60, 180, and 600 min) were used as starting materials and subsequently mixed with Co (6 wt%) and B
Cerâmica. Publicado em: 2022
-
2. Effect of LZSA glass-ceramic addition on the erosive wear of pressureless sintered alumina
Abstract This study aims to evaluate the influence of the 11.6Li2O-16.8ZrO2-68.2SiO2-3.4Al2O3 (mol%) glass-ceramic addition (LZSA, 7 to 21 vol%) on the erosive wear of alumina in comparison to values of pure alumina obtained from the literature. Thus, composites were prepared from three commercial alumina of different initial particle sizes. Specimens were o
REM, Int. Eng. J.. Publicado em: 2020-06
-
3. Análise da redução da alcalinidade de compósitos cimento-madeira em função da substituição parcial do cimento Portland por pozolanas
RESUMO O objetivo desta pesquisa foi avaliar a redução da alcalinidade de compósitos cimento-madeira, produzido com cimento Portland e partículas residuais de Pinus spp., em função da substituição gradual do cimento Portland pelas pozolanas sílica ativa (SA) metacaulim (MK), cinza volante (CV), escória de alto-forno (EAF), cinza de casca de arroz (
Matéria (Rio J.). Publicado em: 25/11/2019
-
4. Integrated Experimental Approach for Alloying of Surface Layer Ti6Al4V+B4C Metal Matrix Composites using Laser Treatment
Surface engineering applications have brought the titanium and its alloys into the limelight in the manufacturing industries such as the aerospace, automobile, marine, chemical processing industry, nuclear power and biomedical. Despite the growths experienced in the use of this material, it is plagued with poor wear behaviour, especially when in contact with
Mat. Res.. Publicado em: 17/01/2019
-
5. Densification and microstructure of Si3N4-TiN ceramic composites
Abstract Silicon nitride is a ceramic material widely used in various structural applications at high temperatures owing to its excellent combination of mechanical and thermal properties. To increase the application of Si3N4, many researches have been developed to improve its fracture toughness and processing conditions. In this study, the sintering and micr
Cerâmica. Publicado em: 2019-01
-
6. Study of the microstructure and mechanical properties of beta tricalcium phosphate-based composites with alumina addition produced by powder metallurgy
Abstract The use of alumina as a reinforcement in metallic and ceramic matrix is well-known. The purpose of this study was to investigate the effect of alumina addition according to its amount on the microstructural and mechanical behavior of tricalcium phosphate ceramic (TCP), more specifically the β-TCP. Although β-TCP has excellent bioactive and biocomp
REM, Int. Eng. J.. Publicado em: 2017-12
-
7. Dry Sliding Wear Behaviour of Aluminium 5059/SiC/MoS2 Hybrid Metal Matrix Composites
The present study is to investigate the influence of weight percentage of silicon carbide (SiC) (5,10 %, 15%) and particle size (10,20,40µm) of SiC and constant 2% of Molybdenum disulphide(MoS2)is reinforced with aluminium matrix. Wear performance of the composite was carried out through pin-on-disc method to calculate friction coefficient and wear resistan
Mat. Res.. Publicado em: 28/09/2017
-
8. LZS/Al2O3 Glass-Ceramic Composites Sintered by Fast Firing
In this work, nanometric Al2O3 (1-5 vol.%) particles (13 nm, 100 m2/g) were added to a 19.58Li2O•11.10ZrO2•69.32SiO2 (mol%) (3.5 µm, 2.5 m2/g) parent glass-ceramic matrix to prepare composites with the purpose of studying the influence of Al2O3 on their structure, microstructure, mechanical, thermal and electrical properties when sintered by fast firing
Mat. Res.. Publicado em: 15/05/2017
-
9. Ballistic Efficiency of an Individual Epoxy Composite Reinforced with Sisal Fibers in Multilayered Armor
Sisal fibers are among the natural lignocellulosic ones with great impact resistance for potential use in polymer composites. This work evaluates the ballistic efficiency of the distinct individual components of a multilayered armor. These include the front ceramic, the back metallic sheet and the intermediate layer as either the conventional aramid fabric o
Mat. Res.. Publicado em: 23/10/2015
-
10. Influência da adição de nanopartículas de TiO2 na obtenção de compósitos a base de liga AA2014 fabricada via metalurgia do pó / Influence of the addition of TiO2 nanoparticles in the composites formation based AA2014 alloy manufactured by powder metallurgy
Aluminum matrix composites and its alloys, especially AA2014, are widely used in automotive and aeronautics applications. The properties of this are very influenced by hardening treatment, however its use is limited at temperatures above 150C due to loss of properties caused by the growth of precipitates at this temperature. The addition of a new phase, fine
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 20/06/2012
-
11. Produção e caracterização de arcabouços porosos de compósitos hidroxiapatita-titânia (HA-TiO2) para uso em engenharia tecidual óssea / Production and characterization of hydroxyapatite-titanium oxide scaffolds for bone tissue engineering
À medida que há uma melhoria na tecnologia aplicada à saúde humana, a expectativa de vida vem aumentando, mas nem todas as partes do corpo podem manter suas funções com o processo de envelhecimento. É preciso que os ossos e a cartilagem apóiem o envelhecimento do corpo, embora as células que os produzem se tornem menos ativas com o tempo. Outros ór
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 24/05/2011
-
12. Nanoparticle assisted coagulation of aqueous alumina suspensions
Colloidal processing of ceramics offers a high potential to achieve homogeneous microstructures with improved material properties. In this study, a novel forming method is investigated, which was already applied successfully for the fabrication of ceramic matrix composites (CMC), but is also considered to be a suitable direct casting technique for the fabric
Materials Research. Publicado em: 29/11/2011