Crack Growth Rate
Mostrando 1-12 de 19 artigos, teses e dissertações.
-
1. Multi-walled carbon nanotube reinforced polymer as a bonded repair for Al 2024-T3 fatigue crack growth
ABSTRACT The influence on multi walled carbon nanotubes (MWCNT, or simply CNT) as a reinforcement material in an epoxy resin in order to decrease the fatigue crack propagation rate in the 2024 T3 aeronautical Al alloy was studied. CT samples were pre-cracked in a resonant fatigue machine until a 4 mm pre-crack length. Four groups of samples were considered:
Matéria (Rio J.). Publicado em: 06/12/2018
-
2. Influencia del tiempo de revenido a 780°C sobre la resistencia al creep del acero ASTM A335 P91
ABSTRACT It has been investigated the effect of tempering time at 780°C on the creep strength of ASTM A335 grade P91 steel. The tempering temperature corresponded to the industrial tempering temperature and the times evaluated were chosen in such a way to accumulate, between the tempering prior as received (40 min) and the treatment carried out in the labor
Matéria (Rio J.). Publicado em: 19/07/2018
-
3. Effect of grinding and aging on subcritical crack growth of a Y-TZP ceramic
Abstract This study aimed to investigate slow crack growth (SCG) behavior of a zirconia ceramic after grinding and simulated aging with low-temperature degradation (LTD). Complementary analysis of hardness, surface topography, crystalline phase transformation, and roughness were also measured. Disc-shaped specimens (15 mm Ø × 1.2 mm thick, n = 42) of a ful
Braz. oral res.. Publicado em: 03/05/2018
-
4. Effect of Interrupted Ageing and Retrogression-Reageing Treatments on Fatigue Crack Growth with a Single Applied Overload in 7050 Aluminum Alloy
The influences of interrupted ageing and retrogression and re-ageing heat treatments on fatigue crack growth with a single applied overload in 7050 aluminum alloy were investigated. The main aims were: to evaluate the influence of these heat treatment conditions on tensile properties, mainly fatigue crack growth rate and fracture process in the low-moderate
Mat. Res.. Publicado em: 19/04/2018
-
5. Fatigue Strength and Fatigue Fracture Mechanism for Spot Welds in U-Shape Specimens
Abstract In this paper, the fatigue behavior of the metallic welded U-shape specimens subjected to cyclic loading have been investigated via experimental and numerical analysis. To do so, two sets of the spot welded specimens with different sizes were prepared and fatigue tests were conducted under the various cyclic loads. The crack propagation is numerical
Lat. Am. j. solids struct.. Publicado em: 2016-12
-
6. Numerical Modelling of Crack Propagation in Cement PMMA: Comparison of Different Criteria
Modelling of a crack propagating through a finite element mesh under mixed mode conditions is of prime importance in fracture mechanics. In this paper, three different crack growth criteria and the respective crack paths prediction in the cement mantle of the reconstructed acetabulum are compared. The maximum tangential stress (MTS) criterion, the minimum st
Mat. Res.. Publicado em: 04/07/2016
-
7. Environmentally-assisted Fatigue Crack Growth in AA7050-T73511 Al Alloy and AA2050-T84 Al-Cu-Li Alloy
The aim of this study was to evaluate and compare the effect of low temperature and saline environment on the fatigue crack growth behavior of the AA7050-T7451 Al alloy and the recently developed AA2050-T Al-Cu-Li alloy. Fatigue at room and low temperature and corrosion-fatigue tests were carried out using an applied stress ratio (R) of 0.1, 15 Hz frequency
Mat. Res.. Publicado em: 04/12/2015
-
8. Normalizing effect on fatigue crack propagation at the heat-affected zone of AISI 4140 steel shielded metal arc weldings
The fractography and mechanical behaviour of fatigue crack propagation in the heat-affected zone (HAZ) of AISI 4140 steel welded using the shielded metal arc process was analysed. Different austenitic grain size was obtained by normalizing performed at 1200 °C for 5 and 10 hours after welding. Three point bending fatigue tests on pre-cracked specimens along
Mat. Res.. Publicado em: 02/04/2013
-
9. Estudo da corrosão e corrosão-fadiga em ligas de Al e Al - Li de alta resistência para aplicação aeronáutica / Study behaviour of corrosion and corrosion fatigue in high strength Al and Al - Li alloys for aeronautic application
The aircraft industry is constantly looking for improved materials which offer benefits in terms of performance, weight and cost savings. Corrosion and fatigue of aluminium alloys are major issues in the service life assessment of aircraft structures and in the management of aging air fleets. The aim of this study was to evaluate the corrosion and corrosion
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 03/09/2012
-
10. Reliability prediction for structures under cyclic loads and recurring inspections
Abstract: This work presents a methodology for determining the reliability of fracture control plans for structures subjected to cyclic loads. It considers the variability of the parameters involved in the problem, such as initial flaw and crack growth curve. The probability of detection (POD) curve of the field non-destructive inspection method and the cond
J. Aerosp. Technol. Manag.. Publicado em: 2009-12
-
11. Avaliação da Tenacidade à Fratura e da Resistência à Fadiga de Dois Aços Utilizados em Eixos de Carros Torpedos
Fatigue and fracture of railway shafts are technical problems that have been treated in studies of mechanical behavior of materials. The pugh car shafts fracture during operation causes production losses and high cost to replace them. In this work, it has been studied the fracture toughness through CTOD parameter and the fatigue crack growth da / dNxΔK
Publicado em: 2008
-
12. Influencia do teor de carbono na propagação de trinca por fadiga e na tenacidade a fratura em camada cementada em aços de alta resistencia mecanica / Influence of the carbon content on propagation in cracks of fadigue and on fracture toughness in carburized case in high strenght steels
Este trabalho propõe uma metodologia para avaliar pontualmente as variações de tenacidade à fratura e taxa de crescimento de trinca de fadiga ao longo da camada cementada de um aço SAE 4320. A pequena espessura dessas camadas impede a retirada de corpos de prova nas dimensões especificadas pelas normas de ensaios de tenacidade à fratura. Assim, para s
Publicado em: 2008