Ferritic Nodular Cast Iron
Mostrando 1-3 de 3 artigos, teses e dissertações.
-
1. Analysis of the application potentiality of nodular cast iron ASTM A536 60-40-18 as raw material for thixoforming processes / Estudo da potencialidade da aplicação do ferro fundido nodular ASTM A536 60-40-18 como materia prima para processos de tixoconformação
This work analyses the thixoability, the viability of actual production of thixotropic semi-solid of ferritic nodular cast iron ASTM A536 60-40-18, as well as the phase transformations taking place in the process. Thixoability evaluation is made through thermal analysis by Differential Thermal Analysis (DTA) and Differential Scanning Calorimetry (DSC) tests
Publicado em: 2009
-
2. CORRELAÇÃO ENTRE MICROESTRUTURA E VIDA-FADIGA EM FERROS FUNDIDOS NODULARES / CORRELATION BETWEEN MICROSTRUCTURE AND FATIGUE LIFE IN NODULAR CAST IRONS
Esta pesquisa teve como objetivo avaliar a vida-fadiga de dois ferros fundidos nodulares modificados metalurgicamente, sendo uma classe predominantemente ferrítica e outra.perlítica. Inicialmente, amostra dos dois ferros fundidos nodulares ferrítico e perlítico foram fundidas adotando-se moldação em areia na geometria padrão Y-block. Em seqüência, c
Publicado em: 2004
-
3. FATIGUE LIFE OF A FERRITIC NODULAR CAST IRON OF DIFFERENT MICROSTRUCTURES. / VIDA EM FADIGA DE UM FERRO FUNDIDO NODULAR FERRÍTICO COM VARIAÇÕES MICROESTRUTURAIS
Esta pesquisa teve como objetivos promover variações microestruturais em um ferro fundido nodular ferrítico tipo ASTM A536 60-40-18, pelo do uso de resfriadores durante a solidificação do material e pela adoção de tratamentos térmicos pós-fundição, bem como avaliar a influência de tais variações microestruturais sobre as propriedades mecânicas
Publicado em: 2003