Hsla Weld
Mostrando 1-5 de 5 artigos, teses e dissertações.
-
1. Evaluación del Deterioro de los Electrodos al Incrementar el Número de Pulsos del Tiempo de Soldadura en Aceros IF y HSLA Galvanizados y la Afectación de las Propiedades Mecánicas en los Puntos de Soldadura
Abstract: Resistance welding points, is the most important method in the assembly industry of unibody because of its automation, which is defined as the ability of the structure to provide adequate protection to passengers against injury from a collision, mainly depends on the mechanical performance of the weld nugget. To extend the life of vehicles produced
Soldag. insp.. Publicado em: 05/01/2017
-
2. WELDABILITY ANALISES OF API 5L X-80 STEEL USING TEKKEN TEST AND IMPLANT TEST / ANÁLISE DA SOLDABILIDADE DO AÇO API 5L X-80 POR MEIO DOS TESTES TEKKEN E DE IMPLANTE
This work shows a study of the weldability of API 5L X-80 steel using the Tekken Test and the Implant Test. The research analises the weldability of HSLA X-80 steel for orbital circunferencial welding with the Shielded Metal Arc Weld and the Flux Core Arc Weld processes with regard to hydrogen induced cracking formation. The aim is to make feasible different
Publicado em: 2008
-
3. The effect of the intercritical heat tretament on the microstructure and mechanical properties of the API 5L X65 steel / Influencia de tratamentos termicos intercriticos na microestrutura e propriedades mecanicas do aço API 5L X65
The intercritical heat treatment effect on the microstructure and mechanical properties of the API 5L X65 steel, widely used in oil and gas pipeline, was investigated. Many researchers have suggested the existence of local brittle zones in the intercritical heat treatment zone (haz) of C-Mn and HSLA (high strenth low alloy) steels of single and multipass wel
Publicado em: 2006
-
4. Fatigue properties of high strength low alloy steel weld metals with different microstructural composition. / Propriedades de fadiga de soldas de alta resistência e baixa liga com diferentes composições microestruturais.
Foram estudadas as propriedades de fadiga em dois grupos de soldas de alta resistência e baixa liga com diferentes composições microestruturais. As soldas do grupo A apresentaram microestruturas compostas de ferrita acicular, ferrita alotriomórfica e ferrita de Widmanstätten, com limite de escoamento de aproximadamente 460 MPa, enquanto que as soldas do
Publicado em: 1999
-
5. Avaliação da tenacidade à fratura de soldas de alta resistência e baixa liga pelo método da integral-J. / Evaluation of high strength low alloy steel weld metal fracture toughness using the J-integral method.
The influence of the microstructure on the fracture toughness behaviour of two groups of multipass High Strength Low Alloy (HSLA) steel weld metals, presenting different microstructure composition, was evaluated. The weld metals A1/A2 exhibited a microstructure composed by acicular ferrite, allotriomorphic ferrite, Widmanstätten ferrite and microphases, and
Publicado em: 1998