1. Microstructure and Thermal Analyses of Cu87-xAl13Nbx High-Temperature Shape Memory Alloys
This paper presents a thermal and microstructural characterization of Cu87-xAl13Nbx (wt%) high temperature shape memory alloys (HTSMA), with Nb contents ranging from 1 to 3%. The alloys were obtained by arc melting under argon atmosphere. Thermal characterization was performed by differential scanning calorimetry (DSC), revealing that the phase martensitic t
Mat. Res.. Publicado em: 28/11/2019
-
2. Mechanically Induced Martensitic Transformation of Hot Rolled and Annealed 304L Austenitic Stainless Steel at Room and Cryogenic Temperatures
The 304L austenitic stainless steel is susceptible to mechanically induced martensitic transformation from slightly above room temperature down to cryogenic temperatures. In this work, austenitic 304L steel produced by two different thermomechanical processes, hot rolling (HR) and cold rolling and annealing (CR/A), were subjected to martensitic transformatio
Mat. Res.. Publicado em: 30/09/2019
-
3. Determination of phases and residual stresses after martensitic transformation induced by rolling in 304L stainless steel
RESUMO O aço inoxidável austenítico 304L é suscetível à transformação martensítica induzida por deformação. Esta transformação de fases depende da temperatura, assim como do modo, taxa e nível de deformação. Neste trabalho as fases e tensões residuais de um aço TRIP 304L, em que a transformação martensítica foi induzida por laminação a
Matéria (Rio J.). Publicado em: 16/09/2019
-
4. Evaluation of two-step transformation in Ni-rich titanium-nickel alloys using thermal and internal friction analyses
ABSTRACT The use of Ti-Ni memory alloys covers several fields of application such as medicine, dentistry, actuators, sensors among others. Because of the thermomechanical behavior of these materials, they are an object of continuous studies and their properties are related to the occurrence of thermoelastic martensitic phase transformations. The thermal anal
Matéria (Rio J.). Publicado em: 16/09/2019
-
5. Análise comparativa entre a têmpera e partição versus a têmpera e revenimento para o aço SAE 4340
RESUMO Um novo tratamento térmico tem sido pesquisado recentemente, cuja denominação é têmpera e partição (T&P), com o intuito de criar aços com austenita estável em sua microestrutura. Inicialmente, esse tratamento foi realizado em aços de alto silício, não obstante, seu potencial alcança outros diversos materiais como os de baixa liga contendo
Matéria (Rio J.). Publicado em: 16/09/2019
-
6. Efeitos da variação da concentração de solução polimérica aquosa a base de PVP na têmpera de aço AISI 4140
RESUMO A têmpera é um tratamento térmico que tem como principal objetivo a elevação de dureza e resistência mecânica dos aços por meio da sua transformação microestrutural. O processo se baseia na elevação da temperatura do material até a austenitização, seguida do arrefecimento por meio da imersão em um fluido, a qual precisa ser rápida o s
Matéria (Rio J.). Publicado em: 16/09/2019
-
7. Effects of composition on transformation temperatures and microstructure of Ni-Ti-Hf shape memory alloys
Abstract High transformation temperature shape-memory alloys (HTSMA) usually present a martensitic transformation temperature (Ms) starting at 100 ºC. That is the case of high nickel Ni-Ti-Hf alloys. This article presents experimental results obtained from arc melting of Ni50Ti50-XHfX .at% (X = 8, 11, 14, 17 and 20 .at%) alloys. This process homogenized eve
REM, Int. Eng. J.. Publicado em: 2019-06
-
8. Efeito da taxa de resfriamento sobre a formação de martensita em um aço inoxidável ferrítico com 11 %Cr e baixos teores de intersticiais
RESUMO Estudou-se o efeito da taxa de resfriamento sobre a cinética de formação da martensita e sua evolução microestrutural em um aço inoxidável ferrítico com 0,011 %C - 11,1 %Cr - 0,013 N, usando a técnica de dilatometria e a microscopia ótica. Amostras foram austenitizadas a 1000°C por um minuto, seguida de resfriamento sob várias taxas até a
Matéria (Rio J.). Publicado em: 20/05/2019
-
9. 3D Microstructural Finite Element Simulation of Martensitic Transformation of TRIP Steels
Abstract In this paper the effects of deformation modes on martensitic transformation for TRIP steels which are composed of Ferrite, Bainite and Retained austenite are investigated in the view of the microstructural level. For this porpose the simulations are run for a synthetically generated microstructure which have 55% Ferrit, 35% Bainite and 10% Retained
Lat. Am. j. solids struct.. Publicado em: 30/07/2018
-
10. Impact of Alloy Composition and Thermal Stabilization on Martensitic Phase Transformation Structures in CuAlMn Shape Memory Alloys
Alloys of CuAlMn are known as cheap, high strength shape memory alloys with an excellent damping capacity within their austenitic-martensitic phase transformation, compared to alloy systems like NiTi, CuZnAl or MnCu. But CuAlMn alloys have disadvantage due to generation of voids by a high shrinkage which further increases the existing proneness to stress cra
Mat. Res.. Publicado em: 19/07/2018
-
11. Influence of defects on the irreversible phase transition in the Fe-Pd doped with Co and Mn
ABSTRACT The appearance of BCT martensite in Fe-Pd-based ferromagnetic shape memory alloys, which develops at lower temperatures than the thermoelastic martensitic transition, deteriorates the shape memory properties. In a previous work performed in Fe70Pd30, it was shown that a reduction in defects density reduces the non thermoelastic FCT-BCT transformatio
Matéria (Rio J.). Publicado em: 19/07/2018
-
12. Estudio del comportamiento en enfriamiento continuo del acero martensítico ferrítico de activación reducida F82H
ABSTRACT 9% Cr martensitic-ferritic steels are currently the privileged candidates to manufacture structural components of the so-called Generation IV nuclear fission reactors, because they exhibit very good thermophysical and mechanical properties under neutron irradiation. Along with them, the so-called Reduced Activation Ferritic-Martensitic steels (RAFM�
Matéria (Rio J.). Publicado em: 19/07/2018