Sliding Wear
Mostrando 1-12 de 63 artigos, teses e dissertações.
-
1. Avaliação tribológica de óleos hidráulicos biodegradável e mineral com deslizamento entre as ligas de Cu-Zn e WC-CoCr
RESUMO A correta seleção dos óleos lubrificantes e das superfícies de contato melhoram o desempenho e reduzem o consumo de energia das máquinas Por isso, a engenharia de superfícies propõe novos revestimentos aos quais seu comportamento tribológico combinado com o uso de óleos biodegradáveis em componentes de sistema hidráulicos, não são conheci
Matéria (Rio J.). Publicado em: 25/11/2019
-
2. Reinforced Glass-ceramics: Parametric Inspection of Three-Dimensional Wear and Volumetric Loss after Chewing Simulation
Resumo O objetivo deste estudo foi investigar o desgaste tridimensional, perda volumétrica e rugosidade após a simulação de mastigação de dois materiais vitro-cerâmicos. Discos de dissilicato de lítio (LD, Emax CAD, Ivoclar) e silicato de lítio reforçado com zircônia (ZLS, Vita Suprinity, Vita Zhanfabrick) (n=20/g) foram confeccionados e digitaliz
Braz. Dent. J.. Publicado em: 07/10/2019
-
3. Efeito do metal de adição na resistência ao desgaste por deslizamento de um aço estrutural soldado por GMAW
RESUMO O objetivo do presente trabalho foi avaliar o efeito do metal de adição na soldagem, e das microestruturas resultantes, na resistência ao desgaste de juntas soldadas de um aço estrutural ASTM A242, que possui resistência à corrosão atmosférica e é utilizado na fabricação de vagões destinados ao transporte de minério. As amostras foram sol
Matéria (Rio J.). Publicado em: 16/09/2019
-
4. Nitretação por descargas elétricas da liga Ti-6Al-4V com adição de pó abrasivo SiC ao fluido dielétrico
RESUMO O processo de nitretação que usa Usinagem por Descargas Elétricas é um método que associa a capacidade de usinar superfícies complexas com a obtenção de tratamento termoquímico de nitretação. A fonte de nitrogênio é proveniente da uréia, que compõe o fluido dielétrico juntamente com água deionizada. A liga de titânio Ti-6Al-4V possui
Matéria (Rio J.). Publicado em: 16/09/2019
-
5. Influência da microestrutura na resistência ao desgaste microabrasivo de ligas de F-Cr-C e Fe-Cr-C-Nb
ABSTRACT Neste trabalho é feita uma avaliação da influência do teor de cromo e da combinação do cromo e nióbio em ligas de revestimento duro do tipo Fe-Cr-C, na microestrutura e propriedades que envolvam a resistência ao desgaste microabrasivo. Vários estudos têm sido realizados em busca de informações conclusivas sobre este sistema em condiçõe
Matéria (Rio J.). Publicado em: 20/05/2019
-
6. Integrated Experimental Approach for Alloying of Surface Layer Ti6Al4V+B4C Metal Matrix Composites using Laser Treatment
Surface engineering applications have brought the titanium and its alloys into the limelight in the manufacturing industries such as the aerospace, automobile, marine, chemical processing industry, nuclear power and biomedical. Despite the growths experienced in the use of this material, it is plagued with poor wear behaviour, especially when in contact with
Mat. Res.. Publicado em: 17/01/2019
-
7. Effect of Experimental Parameters on Wear Response of Thermally Sprayed Carbide Based Coatings
Friction and abrasive wear response of WC-12 Co and Cr3C2-25 NiCr coatings was studied. Abrasive wear experiments were conducted with SiC abrasive particles with varying load and sliding speeds. The results were analyzed using SEM, XRD and XPS observations of worn surfaces, wear debris and worn out abrasive paper. Friction coefficient diminished with rise in
Mat. Res.. Publicado em: 08/11/2018
-
8. Influence of Cryogenic Treatment on the Tribological Behaviour of AISI H21 Tool Steel
The aim of the present work was to find out the optimum cryosoaking duration of deep cryogenic treatment to reduce the wear rate. The AISI H21 hot work tool steel specimens were hardened at 1195 ºC, cryotreated at -185 ºC for 6 to 30 h, double tempered at 540 ºC and soft tempered at 100 ºC. The hardness, impact toughness, wear rate and microstructural ch
Mat. Res.. Publicado em: 29/10/2018
-
9. Effect of Bead Overlapping on the Microstructure and Mechanical Properties of CoCrWC Alloy Coatings
In order to protect industrial components, cobalt base alloys are applied as hardfacing material through welding techniques. A large number of papers have shown that controlling the chemical composition is a key point regarding the wear and corrosion resistance of coatings. This paper investigated the effect of bead overlapping on the microstructure and prop
Mat. Res.. Publicado em: 17/09/2018
-
10. Carbon based DLC films: Influence of the processing parameters on the structure and properties
ABSTRACT Hydrogenated carbon-based films, such as DLC (“Diamond Like Carbon”), have interesting properties such as excellent tribological behavior, low friction coefficient, high superficial hardness and good wear resistance; they are chemically inert and highly corrosion resistant. They are deposited by means of PACVD (plasma-assisted chemical vapor dep
Matéria (Rio J.). Publicado em: 19/07/2018
-
11. Study of Mechanical and Wear Behaviour of Hyper-Eutectic Al-Si Automotive Alloy Through Fe, Ni and Cr Addition
Effect of Fe, Ni and Cr addition on the wear behavior of hyper-eutectic Al-Si automotive alloy has been studied. Dry sliding wear tests have been conducted using pin-on-disc wear testing machine under normal loads of 20N and constant sliding speed of 0.64 ms-1. Influence of Fe addition to the base alloy increases the wear rate due to the formation of needle
Mat. Res.. Publicado em: 11/06/2018
-
12. HVOF-sprayed Coating Over AISI 4140 Steel for Hard Chromium Replacement
The replacement of electrolytic hard chrome (EHC) by high velocity oxy-fuel (HVOF) sprayed coatings is investigated due to the toxicity of EHC process. The wear behavior of AISI 4140 steel coated by HVOF-, EHC-process was compared to quenched and tempered (Q&T) steel using a pin-on-disc apparatus. The wear tests were conducted at room temperature, 10 N appli
Mat. Res.. Publicado em: 28/05/2018