Thermomechanical Treatments
Mostrando 1-12 de 17 artigos, teses e dissertações.
-
1. Evaluation of two-step transformation in Ni-rich titanium-nickel alloys using thermal and internal friction analyses
ABSTRACT The use of Ti-Ni memory alloys covers several fields of application such as medicine, dentistry, actuators, sensors among others. Because of the thermomechanical behavior of these materials, they are an object of continuous studies and their properties are related to the occurrence of thermoelastic martensitic phase transformations. The thermal anal
Matéria (Rio J.). Publicado em: 16/09/2019
-
2. Effect of Thermo-Mechanical Treatments on the Microstructure and Mechanical Properties of the Metastable β-type Ti-35Nb-7Zr-5Ta Alloy
In this work, theoretical composition design and thermo-mechanical treatments were combined in order to improve the mechanical compatibility of a biomedical β-type titanium alloy. By applying a composition design theory, cold rolling and low temperature aging, a metastable β-type Ti-35Nb-7Zr-5Ta (wt%) alloy with an elastic modulus of 47 GPa and a yield str
Mat. Res.. Publicado em: 29/10/2018
-
3. Can low-fusing glass application affect the marginal misfit and bond strength of Y-TZP crowns?
Abstract To evaluate the effect of different surface treatments on the marginal misfit and retentive strength between Y-TZP crowns and an epoxy resin. Forty (40) epoxy resin (G10) abutments (height: 5mm, conicity: 60, finish line: large chamfer) with equal dimensions were milled and included in polyurethane to simulate the periodontal ligament. Next, 40 Y-TZ
Braz. oral res.. Publicado em: 07/05/2018
-
4. Development of a Material for Manufacturing a Mold for Plastic Injection
Injection molding is a process used to manufacture high volumes of plastic containers of complex geometric shapes. Although CuBe has always been used, there are currently some alternative alloys such as the CuNiSiCr alloy that has lower manufacturing cost and similar properties. The objective of this paper is to characterize, by techniques of microscopy, the
Mat. Res.. Publicado em: 07/08/2017
-
5. Effect of Spun Velocities and Composition on the R‒phase and Thermomechanical Behavior in Ti‒Ni Ribbons Electrically Heated
This work deals with structural, electrical and mechanical characterization of Ti‒50.13Ni and Ti‒49.62Ni (at.%) shape memory alloys (SMAs) fabricated at different circumferential wheel velocities. The effect of wheel velocity, chemical composition and heat treatments are investigated. The characterization of crystallographic phases of the Ti‒Ni ribbons
Mat. Res.. Publicado em: 08/04/2016
-
6. Thermomechanical Analysis on Ti-Ni Shape Memory Helical Springs Under Cyclic Tensile Loads
Shape memory alloys (SMAs) present some characteristics, which make it unique material to be use in applications that require strength and shape recovery. This alloys was been used to manufacture smart actuators for mechanical industry devices and several other applications in areas as medicine, robotics, aerospace, petroleum and gas industries. However it i
Mat. Res.. Publicado em: 2015-12
-
7. Study of phase transformations In API 5L X80 Steel in order to increase its fracture toughness
Phase transformations in API 5L X80 steel were studied in different thermomechanical sequences with a view to increasing the fracture toughness of this steel. Dilatometry tests performed on the quenched steel detected a phase transformation occurred, during heating, in the temperature range 593-618 K. This phase transformation was identified as the dissoluti
Mat. Res.. Publicado em: 19/02/2013
-
8. Heat treatments and thermomechanical cycling influences on the R-phase in Ti-Ni shape memory alloys
This article studies changes observed on the R-phase thermoelastic behavior in a near-equiatomic Ti-Ni shape memory alloy. Three kinds of procedures have been performed: different treatments, thermomechanical cycling under constant loading in shape memory helical springs and thermal cycling in as-treated and trained samples. Several heat treatments were carr
Materials Research. Publicado em: 2010-09
-
9. Caracterização de liga metálica a base de alumínio - magnésio obtida por método convencional após tratamentos termomecânicos visando estruturas microcristalinas / Characterization of aluminum magnesium base metallic alloy obtained due conventional after thermomechanical treatments aiming microcrystalline structures
O objetivo deste trabalho é a caracterização mecânica e microestrutural por microscopia óptica e eletrônica, bem como testes de microdureza da liga Al-6063 após tratamentos termomecânicos. As ligas de Al-Mg recebem especial atenção devido a sua leveza, propriedades mecânicas e reciclabilidade. Tais ligas apresentam boas propriedades mecânicas qua
Publicado em: 2008
-
10. Formação de grãos ferríticos ultrafinos através de transformação de fase induzida por deformação / Ultrafine ferrite grains formation through dynamic straininduced transformation
One of the key points in steel development has been the refinement of the microstructure, however without change the chemical composition with addition of alloy elements. The refinement of the ferrite grain size leads simultaneously to an increase in strength and toughness. Ultrafine grains can be produced through thermomechanical controlled treatments, gene
Publicado em: 2007
-
11. Expansão térmica sintonizável do ZrW2O8
Zirconium tungstate (a-ZrW2O8) exhibits isotropic negative thermal expansion over a wide range of temperature. Under high-pressures this material transforms to a metastable amorphous phase (a-ZrW2O8). a-ZrW2O8 can be fully recovered by annealing the amorphous phase at temperatures slightly above 600oC, at room pressure. The amorphous phase, in principle, sho
Publicado em: 2007
-
12. Estudo dos fenômenos que ocorrem durante o recozimento dos aços inoxidáveis austeníticos 304L e 316L deformados em várias temperaturas. / Study of the phenomena that occur during the annealing of worked AISI 304L and 316L austenitic stainless steels deformed at various temperatures.
Hot rolled AISI 304L and 316L austenitic stainless steel sheets, 6mm thick, presented recrystallized equiaxial grains with austenite and islands of delta ferrite, in larger quantities mainly in the center of both steel sheets. The austenite had a weak texture, with a gradient through the thickness. The solution annealing eliminated delta ferrite, however it
Publicado em: 2006