1. Length Scale of the Dendritic Array Tailoring Strength of a 5052 Aluminum Alloy
The present research aims to characterize 5xxx alloy series, considering chemistries based on the commercial 5052 alloy with three Mg contents (2.4wt.%, 2.6wt.% and 3.2wt.%) through transient directional solidification experiments. Very representative incoming impurities to a given twin-roll casting procedure were reached. As such, the Si, Fe, Cu, Mn and Cr-
Mat. Res.. Publicado em: 03/12/2018
-
2. Numerical Analysis of Twin-Roll Casting of Strips With Profiled Cross-Section
The relatively high production costs of innovative materials with tailored properties such as Tailor Welded Blanks, Patchwork Blanks, Tailor Heat Treated Blanks and Tailor Rolled Blanks are responsible for a growing interest in new cost-effective production methods. One of the promising energy-saving and environmental friendly technologies for the production
Mat. Res.. Publicado em: 16/04/2018
-
3. Effect of casting mode and thermal treatments on the electrical conductivity of the AA4006 aluminum alloy
Abstract Initially studied was the effect of the casting mode on the electrical conductivity of AA4006 aluminum alloy sheets produced by both Twin Roll Casting (TRC) and by the semi-continuous Direct Chill (DC) industrial processes, when compared to sheets with commercial purity (AA1050) and high purity aluminum (AA1199). Then, the effects of heat treatments
REM, Int. Eng. J.. Publicado em: 2017-12
-
4. Microstructure and Mechanical Properties of Severely Deformed Mg-4.5Al-1.0Zn Alloy Processed by Asymmetric Rolling on Ingot and Twin Roll Cast Strip
The twin roll cast Mg-4.5Al-1.0Zn alloy sheets, processed by asymmetric rolling and subsequent annealing were investigated. The asymmetric rolling on Mg-4.5Al-1.0Zn ingot was also studied for comparison in terms of microstructure, texture and mechanical properties of the sheets. The results can be summarized as follows. The rolled sheets show intensively def
Mat. Res.. Publicado em: 05/02/2016
-
5. Effect of Warm Rolling on Microstructure and Mechanical Properties of Twin-roll Casted ZK60 Alloy Sheets
In this study, ZK60 magnesium alloy strips were produced by twin roll casting (TRC) and then subjected to warm rolling at the temperature of 300 °C and 350 °C. Rolled sheets related to different rolling reductions were prepared after sequential warm rolling with the rolling speed of 5 m/min. Microstructures, texture, hardness, tensile properties of the rol
Mat. Res.. Publicado em: 2015-04
-
6. Estudo da microestrutura, da textura cristalográfica e da recristalização em chapas obtidas por lingotamento contínuo e semicontínuo da liga de alumínio AA4006. / A study of the microstructure, crystallographic texture, and recrystallization in AA4006 alloy strips produced by twin roll caster and direct chill processes.
A liga de alumínio designada AA4006 é muito utilizada na indústria. É uma liga do sistema Al-Fe-Si, com teores (% em massa) de Si na faixa de 0,8 a 1,2% e Fe entre 0,5 e 0,8%. Apesar de ser bastante utilizada, ela foi pouco estudada. Neste trabalho foi realizado um estudo comparativo da microestrutura e da textura cristalográfica entre chapas da liga AA
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 29/02/2012
-
7. Um estudo comparativo entre chapas produzidas pelos processos de lingotamento contínuo e de lingotamento semicontínuo da liga AA4006: microestrutura e textura cristalográfica
Nesse trabalho, foi realizado um estudo comparativo da microestrutura e da textura cristalográfica entre chapas da liga AA4006 produzidas por dois processos industriais de lingotamento: contínuo (Twin roll caster TRC) e semicontínuo (Direct chill DC). Para a caracterização microestrutural, foram utilizadas as técnicas de microscopia óptica com luz pol
Rem: Revista Escola de Minas. Publicado em: 2012-06
-
8. Texture analysis of cold rolled and annealed aluminum alloy produced by twin-roll casting
A 7.4 mm thick strip of 3003 aluminum alloy produced by the industrial twin-roll casting (TRC) process was homogenized at 500 °C for 12 hours, after which it was cold rolled in two conditions: 1) to reduce the strip's thickness by 67%, and 2) to reduce it by 91%. The alloy was annealed at 400 °C for 1 hour in both conditions. The results revealed that a ro
Materials Research. Publicado em: 22/12/2011
-
9. Modelagem física do sistema de alimentação do processo Twin Roll para lingotamento contínuo de tiras de aço inoxidável
Entende-se, por modelagem de processo, o desenvolvimento de uma representação quantitativa ou qualitativa dos fenômenos físicos associados ao processo. O tipo e a forma do distribuidor, o controle do fluxo e o posicionamento de obstáculos são importantes fatores no projeto do sistema de alimentação de metal líquido para o lingotamento contínuo de t
Publicado em: 2010
-
10. Um estudo comparativo sobre a recristalização de chapas de alumínio AA1200 e AA3003 obtidas por lingotamento contínuo (twin roll caster) e por fundição de placas (direct chill). / A comparative recrystallization study of aluminium sheet AA1200 and AA3003 obtained by continuous casting (twin roll caster) and by casting of plates (direct chill).
A necessidade de redução de custos de produção torna o caster mais vantajoso que o processo de placas, porém a aplicação dos produtos obtidos via vazamento contínuo é limitada pelas condições microestruturais. A alta taxa de resfriamento no processo de vazamento, que pode ultrapassar 300 °C/s, resulta em uma condição de supersaturação dos ele
Publicado em: 2009
-
11. Efeito dos teores de Mn e de Fe na evolução microestrutural de duas ligas do sistema Al-Fe-Mn-Si obtidas por fundição contínua de chapas (Twin Roll Caster)
Com o crescimento constante da utilização do processo twin roll caster para a obtenção de chapas de alumínio, torna-se cada vez mais necessário um melhor conhecimento das características das chapas obtidas por este processo. Foram estudadas, nesse trabalho, duas ligas não tratáveis termicamente, 3003 (1,2%Mn; 0,6%Fe) e 8106 (0,4%Mn; 1,5%Fe). As amos
Rem: Revista Escola de Minas. Publicado em: 2008-06
-
12. Caracterização da liga comercial de alumínio 3003 produzida por fundição contínua de chapas ("twin roll caster"): textura cristalográfica
Nesse trabalho, são apresentados os resultados da determinação de textura cristalográfica da liga comercial de alumínio 3003, produzida em escala industrial pelo processo de fundição contínua de chapas. As diferentes etapas de processamento dos materiais metálicos, tais como solidificação, deformação plástica e recristalização, por exemplo, c
Rem: Revista Escola de Minas. Publicado em: 2007-09