1. Preparation, structural and electrochemical properties of V2O5-WO3 xerogel composite / Obtenção, caracterização e estudos das propriedades de compósitos formados por xerogéis de pentóxido de vanádio e óxido de tungstênio
Vanadium pentoxide xerogel has a bi-dimensional structure which is suitable for intercalation of a variety of ions, organic compounds, and even polymeric species. In addition, when associated with other metal oxides such as WO3 and MoO3, it presents an important role in catalysis, since the resulting oxides act as promoters in catalytic reduction of the NOx
Publicado em: 2007
-
2. Preparação e caracterização de pentóxido de vanádio mesoporoso e reações de intercalação / Synthesis and characterization of mesoporous vanadium pentoxide and intercalation reaction
Synthesis, characterization of vanadium pentoxide mesoporous and studies of properties of hybrids compound based on vanadium oxide xerogel and vanadium pentoxide mesoporous, intercalated with guest species have been the main of this thesis. The interest in those materials, that present a considerable structural and chemical modification, is due to the possib
Publicado em: 2007
-
3. Nanotubos e nanobastões de oxidos e sulfetos de metais de transição obtidos via sistemas bidimensionais (lamelares) : preparação, caracterização e propriedades / Nanotubes and nanorods of transition metal oxides and sulfides obtained from bidimensional systems (layered compunds) : preparation, characteization and properties
This Thesis reports the preparation, characterization and properties of nanotubes and nanorods of transition metal oxides and sulfides obtained from bidimensional (Iamellar) structures. From the structural point view, nanotubes could be formed from bidimensional compounds by rolling its layers generating scroll-like nanotubes, or by the elimination of dangli
Publicado em: 2006
-
4. Influência das condições de síntese nas características e nas propriedades de adsorção de metais do xerogel 3-(1,4-fenilenodiamina)propilsílica
O xerogel híbrido 3-(1,4-fenilenodiamina)propilsílica foi obtido partindo-se de duas quantidades de precursor orgânico (5 e 8 mmol) para 22 mmol de TEOS, na síntese. As amostras dos xerogéis foram caracterizadas usando-se análise elementar CHN, isotermas de adsorção e dessorção de N2 e termoanálise no infravermelho. Os xerogéis foram usados como
Eclética Química. Publicado em: 2005
-
5. Caracterização estrutural e eletrointercalação de íons lítio em compósitos V2O5/gelatina / Structural characterization and electrointercalation of lithium ions in V2O5/gelatin composites
In this work it was prepared and characterized structurally a new composite of vanadium pentoxide xerogel (XRG-V2O5) and gelatin in rate of 1 and 10% in weight (gelatin/V2O5). The xerogel obtained was submitted to drying (80, 200 or 300°C) under vacuum for 4 hours. The structural characterization consisted of X-ray diffraction (XRD), FTIR and Raman spectros
Publicado em: 2004
-
6. Electrochemical behavior and structural changes of V2O5 xerogel
Filmes finos obtidos a partir de xerogel de V2O5 com distintas quantidades de Li+ intercalado eletroquimicamente foram caracterizados utilizando diferentes técnicas in-situ. As mudanças nas propriedades mecânicas foram investigadas utilizando medidas de impedância eletroacústica e estes experimentos indicaram que o processo de intercalação não produz
Journal of the Brazilian Chemical Society. Publicado em: 2003-08
-
7. Development of electrochemical interfaces based on poly(pyrrole) and lamellar vanadium pentoxide xerogel nanocomposites. / "Desenvolvimento de interfaces eletroquímicas à base de nanocompósitos de poli(Pirrol) e xerogel lamelar de pentóxido de vanádio"
Esta tese apresenta um estudo detalhado das propriedades eletroquímicas dos nanocompósitos de V2O5.nH2O e poli(pirrol) sobre a superfície de eletrodos. Demonstramos aqui que pelo controle de parâmetros de síntese é possível alterar a composição das interfaces eletroquímicas dos eletrodos modificados, fazendo com que o poli(pirrol) esteja por cima,
Publicado em: 2001