Mostrando 1-12 de 28 artigos, teses e dissertações.
-
1. Adsorption of Calcium(II), Cadmium(II) and Copper(II) Ions from Water by Prepared Silicon-Aluminum-Zirconium Oxide Using Sol-Gel Process
Ternary oxide silica-alumina-zirconia (SiO2/Al2O3/ZrO2) obtained by the sol-gel process was applied as novel adsorbent of ions in aqueous solution. Batch isotherms were performed using standard CuII, CdII and CaII solutions at variable pH and different concentrations. Adsorption capacity was best at weakly acidic pH. The maximum adsorption capacities were 2.
J. Braz. Chem. Soc.. Publicado em: 2021-07
-
2. Preparation and characterization of yttria stabilized zirconia (YSZ) films deposited by dip-coating on LSM-YSZ substrate with different proportions
ABSTRACT In this work, sol-gel/dip-coating process for obtaining yttria stabilized zirconia (YSZ, ZrO2–8% Y2O3) films deposited onto LSM-YSZ (lanthanum strontium manganite (LSM, La0.7Sr0.3MnO3) mixed with YSZ) with different proportions (20/80, 50/50, 80/20) was investigated. The films were deposited on substrate varying the number of layers deposited. LSM
Matéria (Rio J.). Publicado em: 25/11/2019
-
3. CHARACTERIZATION OF SILICON-ALUMINUM-ZIRCONIUM OXIDE OBTAINED BY THE SOL-GEL PROCESS
A new silicon-aluminum-zirconium ternary oxide (SiO2/Al2O3/ZrO2) was prepared by the sol-gel method followed by one-step washing with absolute ethanol or two-step washing with absolute ethanol followed by ultra-pure water. Both ternary oxides presented high surface area (over 340 m2 g-1). The binding energy values for Zr3d and Al2p levels showed the insertio
Quím. Nova. Publicado em: 18/07/2019
-
4. Effect of sol-gel processing parameters on structure of zirconia
Abstract The present study reports the experimental results regarding the effect of molar ratio of hydrolysis water used in the sol-gel synthesis upon the structure of zirconia. The ZrO2 materials were synthesized via simple metal-chelate route using zirconium n-propoxide [Zr(OCH2CH2CH3)4], n-propanol, acetic acid, and deionized water. Thermogravimetric anal
Cerâmica. Publicado em: 2019-01
-
5. P(VDF-TrFE)/ZrO2 Polymer-Composites for X-ray Shielding
Poly(vinylidene fluoride – tryfluorethylene) [P(VDF-TrFE)] copolymers were mixed with zirconia nanoparticles. The investigation was conducted with the intention to produce nanocompounds with potential to be used as protective patient shielding in radiological procedures. Polymer based nanocomposites with 1, 2, 3, 5 and 10 wt% of ZrO2 nanoparticles were pre
Mat. Res.. Publicado em: 26/02/2016
-
6. SYNGAS PRODUCTION FROM CO2-REFORMING OF CH4 OVER SOL-GEL SYNTHESIZED Ni-Co/Al2O3-MgO-ZrO2 NANOCATALYST: EFFECT OF ZrO2 PRECURSOR ON CATALYST PROPERTIES AND PERFORMANCE
Ni-Co/Al2O3-MgO-ZrO2 nanocatalyst with utilization of two different zirconia precursors, namely, zirconyl nitrate hydrate (ZNH) and zirconyl nitrate solution (ZNS), was synthesized via the sol-gel method. The physiochemical properties of nanocatalysts were characterized by XRD, FESEM, EDX, BET and FTIR analyses and employed for syngas production from CO2-ref
Quím. Nova. Publicado em: 2015-05
-
7. Synthesis and characterization of novel ZrO2-SiO2 mixed oxides
In this study the mixed oxides ZrO2-SiO2, were synthesized by the sol-gel method with a molar ratio of 95:5 (Si/metal) and characterized by X-ray diffraction, absorption-desorption of N2, Fourier transform infrared spectroscopy, thermal gravimetric analysis, temperature-programmed desorption of ammonia, and acidity test by titration. The synthesized material
Mat. Res.. Publicado em: 15/04/2014
-
8. Catalisadores de CuO, Fe2O3 ou Co3O4 suportados em TiO2, CeO2 ou ZrO2: preparação via Sol-gel in situ ou impregnação e avaliação na redução de NO com CO
A minimização das emissões de óxidos de nitrogênio (NOx) é assunto de interesse crucial, pois geram graves problemas ambientais que afetam à saúde humana, à flora e à fauna. Para abater os NOx, processos envolvendo à sua redução catalítica apresentam forte potencial. No caso da redução catalítica de NO com CO, tem-se a vantagem adicional de
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 13/04/2012
-
9. Effects of precursor on the morphology and size of ZrO2 nanoparticles, synthesized by sol-gel method in non-aqueous medium
Pure zirconium oxide (ZrO2) nanoparticles with diameters 10-25 nm were synthesized from ZrOCl2.8H2O and Zr(SO4)2.H2O with benzyl alcohol as non-aqueous solvent medium using sol-gel method. Sodium lauryl sulfate was added as surfactants to control the particle size. The synthesized ZrO2 nanoparticles have a mixture of tetragonal and monoclinic structure. The
Mat. Res.. Publicado em: 09/10/2012
-
10. Caracterização pelo método de rietveld da zircônia tetragonal em sistemas ZrO2-SiO2 obtidos por sol-gel
Materiais a base de zircônia (ZrO2) têm sido empregados como cerâmicas estruturais, revestimento para barreiras térmicas, catalisadores, eletrólitos para células a combustível, dispositivos óticos e eletrônicos, etc. A funcionalidade destes materiais é definida por suas propriedades físico-químicas e mecânicas, muitas das quais podem ser control
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 21/12/2011
-
11. Estudo do óxido misto SiO2/ZrO2/Al2O3 aplicado como inibidor de corrosão do aço carbono
Este trabalho apresenta a síntese do óxido misto SiO2/ZrO2/Al2O3 pelo processo sol gel, visando sua utilização como inibidor de corrosão do aço carbono SAE 1020. A caracterização dos óxidos formados foram realizadas através das análises de Espectroscopia de Infravermelho com Transformada de Fourier (FTIR), Difração de Raios X (DRX) e Microscopia
IBICT - Instituto Brasileiro de Informação em Ciência e Tecnologia. Publicado em: 08/04/2011
-
12. Catalisadores à base de Mo, CoMo e NiMo incorporados por impregnação ou in situ em γ-Al2O3, ZrO2 e γ-Al2O3-ZrO2 Avaliação na hidrodessulfurização do tiofeno
Estudou-se a preparação de catalisadores de HDS à base de Mo, CoMo e NiMo suportados sobre -Al2O3, ZrO2 e -Al2O3-ZrO2. O teor de zircônia incorporada na alumina foi de 20 ou 40 % (m/m). Esses suportes foram sintetizados via sol-gel e a incorporação dos metais realizada por impregnação ou por adição direta dos sais precursores à mis
Publicado em: 2011